Efeito protetor de enxaguatórios com diferentes fluoretos utilizados previamente aos desafios erosivos/abrasivos em esmalte e dentina / Protective effect of solutions with different fluorides used previously to erosive/abrasive challenges in enamel and dentin

Aim: To evaluate the protection offered by commercial mouthwashes containing sodium fluoride or stannous chloride associated with sodium fluoride to enamel and dentin, prior to erosive and abrasive cycling. Materials and Methods: Enamel and dentin samples were obtained from bovine incisors and subdivided into 3 groups (n=10), according to the fluoridated ingredient tested: FS (sodium fluoride - NaF (225 ppm)); FE (tin fluoride - NaF + SnCl2 (800 ppm Sn2+)); control (distilled water). The samples were submitted to an erosive/abrasive cycle with immersion in citric acid (lemon soda for 5 min, 4×/day, 5 days, with remineralization intervals in artificial saliva for 60 min). Abrasion was carried out with an electric brush (200 g/force) after the first and last cycles, 2x/day, and immediately afterward immersed in the tested solutions. Structure loss was obtained by optical profilometry. The data were subjected to analysis of variance and multiple comparison for each substrate separately. Results: For enamel there was a difference between the groups (p = 0.027), with the FS showing less loss of structure compared to the control 2.02 (±0.48). The FE group showed similar loss to the control and FS 2.32 (±0.58)ab. For dentin there was a difference between the groups (p = 0.011), with FE showing less loss of structure compared to the other groups, 0.82 (25% - 0.34; 75% - 0.95). Discussion: The protection of fluorides in erosive/abrasive challenges depends on the type and dental substrate. Conclusion: Mouthwash with sodium fluoride prior to erosive/abrasive challenges caused less loss of enamel surface, while for dentin, sodium fluoride associated with stannous chloride caused less loss of structure.

Objetivo: Avaliar a proteção oferecida por soluções para bochecho de fluoreto de sódio ou cloreto de estanho associado ao fluoreto de sódio ao esmalte e à dentina, previamente à ciclagem erosiva e abrasiva. Materiais e Métodos: Amostras de esmalte e dentina foram obtidas a partir de incisivos bovinos e subdivididas em 3 grupos (n=10), de acordo com o princípio ativo fluoretado testado: FS (fluoreto de sódio - NaF (225 ppm)); FE (fluoreto de estanho - NaF + SnCl2 (800 ppm Sn2+)); controle (água destilada). As amostras foram submetidas a um ciclo erosivo/abrasivo com imersão em ácido cítrico (refrigerante de limão por 5 min, 4×/dia, 5 dias, com intervalos de remineralização em saliva artificial por 60 min). A abrasão foi realizada com escova elétrica (200 g/força) após o primeiro e o último ciclos, 2×/dia, e logo em seguida imersos nas soluções testadas. A perda de estrutura foi obtida por perfilometria óptica. Os dados foram submetidos à análise de variância e comparação múltipla para cada substrato separadamente. Resultados: Para esmalte houve diferença entre os grupos (p = 0,027), tendo o FS apresentados menor perda de estrutura comparado ao controle 2,02 (±0,48). O grupo FE apresentou perda similar ao controle e ao FS 2,32 (±0,58)ab. Para dentina houve diferença entre os grupos (p = 0,011), sendo que o FE apresentou menor perda de estrutura comparado aos demais grupos 0,82 (25% - 0,34; 75% - 0,95). Discussão: A proteção dos fluoretos em desafios erosivos/abrasivos depende do tipo e do substrato dental. Conclusão: O bochecho com fluoreto de sódio previamente aos desafios erosivos/abrasivos apresentou menor perda de superfície em esmalte, enquanto para dentina o fluoreto de sódio associado ao cloreto de estanho apresentou menor perda de estrutura.

Avaliação dos Efeitos da Remoção da Resina Residual e do Polimento na Superfície do Esmalte após Descolagem do Braquete / Evaluation of the Effects of Residual Resin Removal and Polishing on the Enamel Surface after Bracket Debonding

Considerando o uso de brocas para remoção da resina residual após descolagem do braquete e a possibilidade de injúrias à superfície do esmalte após o uso dessas brocas, este trabalho teve como objetivo realizar um estudo experimental, para avaliar a variação do aspecto superficial do esmalte de forma qualitativa, por meio da avaliação com imagens topográficas do esmalte dentário, utilizando-se a Microscopia Eletrônica de Varredura (MEV), a qual permitiu ilustrar e avaliar a superfície do esmalte após a fase de polimento final, realizada por dois métodos: taça de borracha ou escova Robinson. Foram utilizados 25 dentes pré-molares humanos, obtidos a partir de exodontias em pacientes que procuraram voluntariamente o curso de Residência em Cirurgia da Clínica Odontológica Universitária da Universidade Estadual de Londrina. Os dentes foram divididos em quatro grupos: A, B, C e D, contendo 6 dentes cada, de acordo com as brocas utilizadas para a remoção do remanescente adesivo e o polimento escolhido, além de um dente como "controle". Foi avaliada a rugosidade superficial do esmalte após a remoção da resina e a superfície do esmalte após o polimento com as duas opções apresentadas. Os resultados mostraram que, por observação e inspeção, as brocas removeram a resina residual de todos os dentes, porém, causaram riscos e ranhuras, como evidenciado nas imagens em MEV. Concluiu-se que não houve diferença estatística entre os métodos de polimento e que ambos foram importantes para a redução das marcas abrasivas, proporcionando uma superfície mais lisa do esmalte.

Considering the use of specific burs to remove residual resin after bracket debonding and the possibility of injuries to the dental enamel after using these burs, this study aimed to verify the variation in the enamel surface appearance in a qualitative way and evaluation with topographic images of the dental enamel. The use of Scanning Electron Microscopy (SEM) allowed to illustrate and evaluate the enamel surface after the final polishing phase using two methods: rubber cup or Robinson brush. Twenty-five human premolar teeth were obtained from extractions in patients who voluntarily sought the Oral Maxillofacial Surgery Residency at the Dental School from the State University of Londrina; the teeth were divided into four groups A, B, C and D containing 6 teeth each according to the burs used to remove the remaining adhesive and the chosen polishing, in addition to one tooth as a "control". Dental enamel surface roughness was evaluated after resin removal and enamel surface after polishing with the two methods presented. The results showed that by observation and inspection, the burs removed residual resin from all teeth, however, caused scratches and grooves as evidenced in the SEM images. Based on the results, there was no statistical difference between the polishing methods, and both were important for the reduction of abrasive marks and provided a smoother enamel surface.

Dentifrícios branqueadores contendo Blue covarine: revisão de literatura / Bleaching dentifrices containing "Blue covarine" literature review

Introdução: O efeito branqueador dos dentifrícios contendo Blue covarine é fundamentado no seu mecanismo de ação, caracterizado pela sua deposição na superfície dentária, alterando a percepção da cor. Objetivo: Revisar a literatura e buscar evidência científica sobre o efeito branqueador do Blue Covarine em tecidos mineralizados e materiais restauradores estéticos. Materiais e métodos: Para a revisão da literatura foram feitas buscas nas bases de dados PubMed, LILACS, BBO, SciELO e MEDLINE para identificar estudos clínicos e laboratoriais que avaliassem a ação branqueadora do agente óptico Blue covarine. Como estratégia de busca foram utilizados os descritores "Blue covarine", "Blue covarine e pasta de dentes", "Blue covarine and toothpaste", "Blue covarine e dentifrícios", "Blue covarine and dentifrices", "Blue covarine e dentifrícios branqueadores", "Blue covarine and whitening dentifrices", "Blue covarine e dentifrícios clareadores", "Blue covarine and bleaching dentifrices", "Blue covarine e pasta de dentes branqueadoras", "Blue covarine and whitening toothpaste", "Blue covarine e pasta de dentes clareadoras", "Blue covarine and bleaching toothpaste". Resultados: Dois pesquisadores selecionaram e analisaram criticamente 31 artigos, sendo 2 revisões da literatura, 4 estudos clínicos e 25 estudos laboratoriais. Divergências quanto ao desenho de estudo, métodos, amostra, critérios clínicos e parâmetros laboratoriais foram observados, além de conflitos de interesse. Conclusão: O Blue Covarine presente nos dentifrícios branqueadores parece ser efetivo na promoção do branqueamento dentário apenas quando associado aos agentes abrasivos presentes nas formulações, evidenciando que ensaios clínicos e laboratoriais, com metodologias semelhantes, são necessários para se obter evidência científica conclusiva sobre o efeito deste agente branqueador.(AU)

Introduction: The whitening effect of dentifrices containing Blue Covarine is based on its mechanism of action, characterized by its deposition on the tooth surface, altering the perception of color. Objective: To review the literature and seek scientific evidence on the whitening effect of Blue Covarine on mineralized tissues and aesthetic restorative materials. Materials and methods: For the literature review, searches were carried out in the PubMed, LILACS, BBO, SciELO and MEDLINE databases, in order to identify clinical and laboratory studies that evaluated the whitening action of the optical agent Blue Covarine. As a search strategy, the descriptors "Blue Covarine", "Blue Covarine and toothpaste", "Blue Covarine and dentifrices", "Blue Covarine and whitening dentifrices", "Blue Covarine and bleaching dentifrices", "Blue Covarine and whitening toothpaste", "Blue Covarine and bleaching toothpaste". Results: Two researchers selected and critically analyzed 31 articles, including 2 literature reviews, 4 clinical studies and 25 laboratory studies. Differences in study design, methods, sample, clinical criteria and laboratory parameters were observed, in addition to conflicts of interest. Conclusion: Blue Covarine present in whitening dentifrices seems to be effective in promoting dental whitening only when associated with abrasive agents present in the formulations, showing that clinical and laboratory tests, with similar methodologies, are necessary to obtain conclusive scientific evidence on the effect of this bleaching agent.(AU)

Ozone gas therapy for tooth bleaching preserves enamel microhardness, roughness and surface micromorphology / Ozonioterapia gasosa para clareamento dental preserva a microdureza, rugosidade e micromorfologia superficial do esmalte

ABSTRACT After ozone therapy for bleaching, it is important to evalúate enamel surface properties, to ensure that bleaching provides adequate conditions for sound dental substrate. Aim: The aim of this in vitro study was to evaluate the effects of a bleaching treatment with 10% carbamide peroxide (CP), with or without ozone (O), on the microhardness, roughness and micromorphology of the enamel surface. Materials and Method: Bovine enamel blocks were planed and distributed among the following three bleaching treatment groups (n=10): CP - 1 hour per day/14 days (Opalescence PF 10%/ Ultradent); O - 1 hour per day every 3 days/3 sessions (Medplus VPhilozon, 60 mcg/mL and oxygen flow rate of 1 L/min); and OCP - CP with O, 1 hour per day every 3 days/3 sessions. Enamel surface microhardness (Knoop), roughness (Ra), and micromorphology by scanning electron microscopy (5,000x magnificaron) were determined before and after the treatments. Results: ANOVA and Tukey-Kramer's test showed that enamel microhardness remained unchanged by treatment with O and OCP (p=0.0087), but decreased by treatment with CP. Treatment with O promoted higher enamel microhardness than the other groups (p=0.0169). Generalized linear mixed models for repeated measures over time indicated treatment with CP increased enamel roughness more than OCP or O (p=0.0003). CP produced slight irregularities in enamel micromorphology after the whitening treatment. O, with or without CP, maintained the mechanical and physical properties of microhardness and enamel surface micromorphology, and either maintained or reduced surface roughness, compared to the conventional tray-delivered CP bleaching treatment. Conclusions: Treatment with 10% carbamide peroxide in trays promoted greater changes in enamel surface properties than treatments with ozone and with 10% ozonized carbamide peroxide in the office.

RESUMO É importante avaliar as propriedades da superficie do esmalte após a aplicagao da ozonioterapia para clareamento, para garantir que o efeito clareadorproporcione condigoes adequadaspara um substrato dentário higido. Objetivo: O objetivo deste estudo in vitro foi avaliar os efeitos de um tratamento clareador com peróxido de carbamida (PC) a 10%, associado ou nao ao ozonio (O), na microdureza, rugosidade e micromorfologia da superficie do esmalte. Materials e Método: Blocos de esmalte bovino foram aplainados e distribuidos entre tres grupos de tratamento clareador (n=10): PC - 1 hora por dia/14 dias (Opalescence PF 10%/ Ultradent); O - 1 hora por dia a cada 3 dias/3 sessoes (Medplus VPhilozon, 60 mcg/mL e fluxo de oxigenio de 1 L/min); e PCO - CP com O, 1 hora por dia a cada 3 dias/3 sessoes. A microdureza (Knoop), a rugosidade (Ra) e a micromorfologia da superficie do esmalte avaliada por microscopia eletronica de varredura (aumento de 5.000x) foram analisadas antes e após os tratamentos. Resultados: ANOVA e teste de Tukey-Kramer mostraram que O e PCO mantiveram os valores de microdureza do esmalte ao final do tratamento (p=0,0087), enquanto PC promoveu diminuigao da microdureza. O promoveu maiores valores de microdureza do esmalte do que os outros grupos ao final do tratamento (p=0,0169). Modelos lineares generalizados mistos para medidas repetidas no tempo indicaram um aumento na rugosidade da superficie para PC, levando a maior rugosidade do esmalte ao final do tratamento, em comparagao com PCO ou O (p=0,0003). PC apresentou pequenas irregularidades na micromorfologia do esmalte após o tratamento clareador. O, com ou sem PC, manteve as propriedades mecánicas e fisicas de microdureza e micromorfologia da superficie do esmalte, e manteve ou reduziu a rugosidade da superficie, em comparagao com o tratamento clareador a base de PC aplicado em moldeira convencional. Conclusoes: O tratamento com peróxido de carbamida a 10% para uso em moldeiras promoveu maiores alteragoes nas propriedades de superficie do esmalte do que aquelas observadas nos tratamentos com ozonio e com peróxido de carbamida ozonizado a 10% para uso em consultório.

Efeito de doses terapêuticas de radioterapia sobre a morfologia, composição química e microdureza do esmalte e da dentina de dentes permanentes / Effect of therapeutic doses of radiotherapy on the morphology, chemical composition, and microhardness of enamel and dentin of permanent teeth

Introdução: Padrões atípicos de cárie dentária em pacientes submetidos a radioterapia para o tratamento do câncer de cabeça e pescoço podem estar associados aos efeitos da radiação sobre as glândulas salivares e tecidos dentários duros. Somados, podem contribuir para a cárie relacionada a radiação. Embora haja evidências sobre alterações sofridas pelos tecidos dentários duros após radioterapia, não há consenso na literatura sobre a gravidade destas alterações. Objetivo: avaliar a microestrutura, composição química e microdureza do esmalte e da dentina de dentes permanentes submetidos a doses terapêuticas de radioterapia in vitro. Material e métodos: estudo experimental, qualitativo, quantitativo e semiquantitativo. Foram obtidos fragmentos coronários de 24 terceiros molares. Constituiuse 2 grupos: NIR (controle): formado por fragmentos de dentes não irradiados e IVT (irradiado): formado por fragmentos de dentes irradiados in vitro (2 Gy/dia 5 vezes por semana, totalizando 70 Gy). Os fragmentos foram submetidos a análise da microdureza (n=24), Espectroscopia de Infravermelho com Transformada de Fourier (FTIR) (n=24), análise morfológica através de Microscopia Eletrônica de Varredura (MEV) (n=19) e análise de elementos químicos por Espectroscopia de Dispersão de Energia de Raio X (EDX) (n=19). As análises foram feitas antes e após a irradiação. Os dados foram testados para distribuição normal (teste de Shapiro-Wilk, α = 0,05) e igualdade de variâncias (teste de Levene, α = 0,05), seguido de testes estatísticos paramétricos. Para a comparação das variáveis quantitativas foi aplicado o teste T de Student. Um valor de p <0,05 (5%) foi considerado estatisticamente significativo. Resultados: em relação as propriedades mecânicas observamos redução significativa da microdureza do esmalte e dentina após irradiação (p<0,001). A análise da composição química por FTIR mostrou que no esmalte não houve alteração da razão matriz/mineral (M:M) no grupo irradiado (p<0,821), mas houve redução significativa do teor relativo de carbonato (RCC) após irradiação (p<0,039). Na dentina observamos redução significativa da razão matriz/mineral (M:M) e carbonato/mineral (C:M) no grupo irradiado (p<0,001), enquanto a razão amida I/amida III, não sofreu alteração significativa após irradiação (p<0,536). Na análise de EDX realizadas no esmalte, não observamos variação no conteúdo de cálcio e fósforo após radiação, mas a razão Ca/P mostrou-se significantemente mais elevada no grupo irradiado (p<0,001). Na dentina, não houve alteração do teor de cálcio e fósforo, assim como da razão Ca/P após irradiação (p<0,267). A análise morfológica através de MEV pós irradiação, mostrou que no esmalte a maioria das amostras apresentaram uma alteração das características microestruturais com a presença de microporosidades, perda de padrões regulares das áreas prismáticas e interprismáticas e presença de áreas amorfas. Na dentina observamos manutenção do padrão de dentina peritubular e intertubular, com a presença de túbulos dentinários desobliterados e com a rede de fibras colágenas mais evidente grupo irradiado. Conclusão: as doses terapêuticas de radioterapia provocaram redução da microdureza, alterações na microestrutura e composição química do esmalte e da dentina. Assim, inferimos que doses terapêuticas de radiação exercem um impacto negativo sobre as propriedades mecânicas, químicas e micro-morfológicas dos tecidos dentários duros aumentando a vulnerabilidade destes tecidos à cárie relacionada a radiação.

INTRODUCTION: Atypical patterns of dental caries in patients undergoing radiotherapy to treat head and neck cancer may be associated with the effects of radiation on salivary glands and dental hard tissues. Together, they can contribute to radiation-related caries. Although there is evidence of changes in hard dental tissues after radiotherapy, there is no agreement in the literature on the severity of these changes. PURPOSE: This study aims to evaluate the microstructure, chemical composition, and microhardness of enamel and dentin in permanent teeth subject to therapeutic doses of in vitro radiotherapy. MATERIAL AND METHODS: This is an experimental, qualitative, quantitative, and semi-quantitative study. Coronary fragments were obtained from 24 third molars. Two groups were created: NIR (control), including fragments of non-irradiated teeth, and IVT (irradiated), including fragments of in vitro irradiated teeth (2Gy/day five times a week, totaling 70Gy). The fragments underwent microhardness analysis (n =24), Fourier-transform Infrared Spectroscopy (FTIR) (n=24), morphological analysis by Scanning Electron Microscope (SEM) (n=19), and analysis of chemical elements by Energy-dispersive X-Ray Spectroscopy (EDX) (n=19). The analyses were performed before and after irradiation. Data were tested for normal distribution (ShapiroWilk test, α = 0.05) and equality of variances (Levene test, α = 0.05), followed by parametric statistical tests. The Student's T test was applied to compare the quantitative variables. A pvalue < 0.05 (5%) was considered statistically significant. RESULTS: Concerning the mechanical properties, we observed a significant reduction in enamel and dentin microhardness after irradiation (p<0.001). The analysis of the chemical composition by FTIR showed no change in the mineral/matrix ratio (M:M) in enamel in the irradiated group (p<0.821), but there was a significant reduction in the relative carbonate content (RCC) after irradiation (p<0.039). In dentin, we observed a significant reduction in the mineral/matrix ratio (M:M) and carbonate/mineral ratio (C:M) in the irradiated group (p<0.001). In contrast, the amide I/amide III ratio showed no significant change after irradiation (p<0.536). In the EDX analysis performed on enamel, we did not observe any calcium and phosphorus content variation after radiation. However, the Ca/P ratio was significantly higher in the irradiated group (p<0.001). In dentin, there was no change either in calcium and phosphorus contents or in the Ca/P ratio after irradiation (p<0.267). The morphological analysis through SEM after irradiation showed that there is a loss in the characteristics of the enamel surface of most fragments, with the presence of microporosities, loss of regular patterns of the prismatic and interprismatic areas, and the presence of amorphous areas. In dentin, we observed maintenance of the peritubular and intertubular dentin patterns, with the presence of unobliterated dentinal tubules and with the most evident network of collagen fibers in the irradiated group. CONCLUSION: Therapeutic doses of radiotherapy caused a reduction in microhardness and changes in the microstructure and chemical composition of enamel and dentin. Thus, we conclude that therapeutic doses of radiation have a negative impact on the mechanical, chemical, and micromorphological properties of hard dental tissues, increasing the vulnerability of these tissues to radiation-related caries

Restoration of molars affected by molar-incisor hypomineralization using the occlusal replica technique / Restauração de molares afetados pela Hipomineralização Molar-Incisivo utilizando a técnica da réplica oclusal

ABSTRACT The aim of this study was to report the clinical case of an 8-year-old male patient seen at the Pediatric Dentistry outpatient clinic at the Universidade Federal do Paraná, Brazil, diagnosed with molar-incisor hypomineralization (MIH) after presenting with pain in teeth 16, 36, and 46, which had extensive atypical cavities and opacities on the adjacent enamel. A diagnostic wax-up of affected teeth was performed for manufacture of silicone occlusal matrix. Encapsulated high-viscosity glass ionomer cement was handled and inserted into the occlusal matrix which was fitted onto the teeth by slight finger pressure. After setting time, excess of material was removed, and occlusion was checked. A flowable resin coating material was applied, and the restorations were finished. Six months later, the restorations performed for treatment of the severe MIH lesions proved to be efficient, lowering the sensitivity reported by the patient, reshaping the teeth, improving their function, and refining dental esthetics.

RESUMO O objetivo deste estudo foi relatar um caso clínico de um paciente com diagnóstico de Hipomineralização de Molares e Incisivos (HMI). Paciente do sexo masculino, de 8 anos de idade, compareceu à clínica de Odontopediatria da Universidade Federal do Paraná com queixa de dor nos dentes 16, 36 e 46 - os quais apresentavam extensas cavitações atípicas com opacidades no esmalte adjacente. O enceramento diagnóstico dos dentes afetados foi realizado para a confecção das matrizes oclusais de silicone. Cimento ionômero de vidro de alta viscosidade encapsulado foi manipulado e inserido na matriz oclusal, a qual foi encaixada sobre os dentes, exercendo-se leve pressão digital. Após a presa do material os excessos foram removidos e a oclusão foi checada. Aplicou-se uma camada de resina fluída de cobertura e as restaurações foram finalizadas. Após seis meses, as restaurações realizadas para tratar as lesões severas de HMI mostraram-se eficazes, reduzindo a sensibilidade relatada pelo paciente, além de reestabelecerem a anatomia, função e estética dentária.

Effect of Stevia rebaudiana Bertoni infusion on enamel demineralization and dental biofilm formation: an in-situ study / Efeito da infusão de Stevia rebaudiana Bertoni na desmineralização do esmalte e na formação do biofilme dental: um estudo in situ

Aim: Stevia rebaudiana Bertoni (Stevia) is a natural non--caloric sweetener that can modify the cariogenicity of biofilms. This study aimed to evaluate the effect of Ste-via infusion in microbial and biochemical composition of biofilms formed in the presence of sucrose and on enamel demineralization. Materials and Methods: In a cross-over design, eleven volunteers wore an intraoral palatal appliance containing 4 slabs of bovine enamel during 3 phases of 7 days each. Sucrose solution (20%) was dripped onto slabs 8 times/day and 0.9% sodium chloride (NaCl), 0.12% chlorhexidine (CHX), or 5% infusion of Stevia were dripped 2x/day. Biofilm formed on the slabs was collected and analyzed for counts of microorganisms (total bacteria, Lactobacilli, Candida spp., and Streptococcus mutans) biochemical composition in terms of soluble and insoluble extracellular polysaccharides and qualitative assessment by scanning electron microscopy. The per-centage of surface hardness loss (%SHL) was determined on enamel slabs taken baseline and post-biofilm Knoop surface hardness values. Results: The % SHL in the CHX treatment was statistically lower in comparison to NaCl (p < 0.05). No differences were found between Stevia and CHX and between Stevia and NaCl. No other difference was found among the experimental groups with respect to the other outcomes. Discussion: Under high carioge-nic conditions resembling frequent exposure to sucrose and absence of mechanical disruption, use of Stevia can neither modify the counts of cariogenic microorganisms nor the concentration of extracellular polysaccharides on in situ formed biofilms. This may have occurred due to the exposure of the biofilm to high sucrose concentration for all treatments and the condi-tion of the microorganism growth in situ, which may hinder the diffusion of substances through the thick biofilm. Conclusion: Biofilm exposed to a high cariogenic challenge and without mechanical disruption is not affected by an infusion of Stevia rebaudiana Bertoni.

Objetivo: A Stevia rebaudiana Bertoni (Stevia) é um adoçante natural não calórico que pode modificar a cariogenicidade de biofilmes. Este estudo teve como objetivo avaliar o efeito da infusão de Stevia na composição microbiana e bioquímica de biofilmes formados na presença de sacarose e na desmineralização do esmalte. Materiais e métodos: Em um desenho cruzado, onze voluntários usaram um aparelho intraoral palatino contendo 4 pla-cas de esmalte bovino durante 3 fases de 7 dias cada. A solução de sacarose (20%) foi gotejada em placas 8 vezes/dia e cloreto de sódio a 0,9% (NaCl), clorexidina a 0,12% (CHX) ou infusão a 5% de Stevia foram gotejados 2x/dia. O biofilme formado nas placas foi coletado e analisado para contagem da composição bioquímica de microrganismos (bactérias totais, Lactobacilos, Candida spp. e Streptococcus mutans) em termos de polissaca-rídeos extracelulares solúveis e insolúveis e avaliação qualitativa por microscopia eletrônica de varredura. A porcentagem de perda de dureza superficial (%SHL) nos blocos de esmalte foi determinada com base nos valores de dureza superficial Knoop tomadas no início e pós-biofilme. Resultados: O % SHL no tratamento CHX foi estatisticamente menor em comparação ao NaCl (p < 0,05). Não foram encontradas diferenças entre Stevia e CHX e entre Stevia e NaCl. Nenhuma outra diferença foi encontrada entre os grupos experimentais em re-lação aos outros resultados. Discussão: Sob condições cariogênicas elevadas que se assemelham a exposição frequente à sacarose e ausência de disrupção mecânica, o uso de Stevia não pode modificar as contagens de microrganismos cariogênicos nem a concentração de polissacarídeos extracelulares em biofilmes formados in situ. Isso pode ter ocorrido devido à exposição do biofilme à alta concentração de sacarose para todos os tratamentos e à condição de crescimento do microrganismo in situ, o que pode dificultar a difusão de substâncias através do biofilme espesso. Conclusão: O biofilme exposto a um alto desafio cariogênico e sem disruptucao mecânica não é afetado por uma infusão de Stevia rebaudiana Bertoni.

Estudo fotoacústico de dentes humanos submetidos à radioterapia / Photoacustic study of human teeth submitted to radiotherapy

Objetivo: Esta pesquisa teve como objetivo a caracterização, pela técnica de Espectroscopia de Absorção Fotoacústica, do efeito da radiação X sobre os tecidos dentais humanos mineralizados, irradiados com doses usada para tratamento de pacientes portadores de câncer de cabeça e pescoço. Materiais e métodos: As radiações foram fornecidas por um acelerador linear em dentes humanos seccionados longitudinalmente, onde a porção central foi investigada em três regiões: esmalte, dentina coronária e dentina cervical, antes e após as irradiações. 20 dentes foram analisados, onde um grupo formado por 10 dentes foi irradiado com dose total de 70 Gy fracionada em doses diárias de 2 Gy, enquanto outro grupo também com 10 dentes foi irradiado com uma dose única de 70 Gy. Resultados: Após a irradiação, foi observada uma redução significativa na difusividade térmica de 47 e 40% no esmalte, 43 e 37% na dentina coronária e 60 e 48% na dentina cervical, para a radiação em dose fracionada e única, respectivamente. Discussão: As medições da difusividade térmica das regiões analisadas, antes de serem irradiadas, mostraram que os valores encontrados estão de acordo com a literatura, enquanto que a forte queda da difusividade mostrou uma degradação da estrutura dentária. Além disso, a aplicação da radiação X gerou danos significativos ao dente que podem propiciar a for-mação e propagação das cáries de radiação. Conclusão: A redução da difusividade térmica observada retarda tanto a dissipação do calor, quanto a velocidade que este atinge as regiões internas do dente, levando a um retardo na sensação da dor, podendo acarretar no uso excessivo de energia durante os procedimentos odontológicos.

Aim: This research aimed to characterize, by the technique of Photoacoustic Absorption Spectroscopy, the effect of X-radiation on mineralized human dental tissues, irra-diated with doses used for the treatment of patients with head and neck cancer. Materials and methods: Radiation was introduced by a linear accelerator in humans teeth longitudinally sectioned, where the central portion was investigated in three regions: enamel, coronary dentin and cervical dentin, before and after irradiation. 20 teeth where analyzed, where a group formed by 10 teeth was irradiated with a total dose of 70 Gy, divided into daily doses of 2 Gy, while another group, also with 10 teeth, was irradiated with a single dose of 70 Gy. Results: After irradiation, a significant reduction in thermal diffusivity of 47 and 40% in enamel, 43 and 37% in coronary dentin and 60 and 48% in cervical dentin was observed for radiation in fractional and single doses, respectively. Discussion: The measures, obtained before the radiation, of thermal diffusivity on the analyzed regions, showed that the values found in this work are in agreement with the literature, while the strong fall in the thermal diffusivity showed that a degradation in the dental structure happened. In addition, the application of X radiation caused significant damage to the tooth that could promote the formation and propagation of radiation caries. Conclusion: The reduction in thermal diffusivity observed slows down both heat dissipation and the speed at which it reaches the internal regions of the tooth, leading to a delay in the sensation of pain, which may result in excessive energy usage during dental procedures.

Análise macroscópica e radiográfica de dentes decíduos com hiperbilirrubinemia de crianças com doenças hepáticas crônicas e transplante hepático / Macroscopic and radiographic analysis of primary teeth with hyperbilirubinemiain children with chronic liver disease and liver transplantation

Objetivo: identificar mediante análise macroscópica e ra-diográfica as alterações estruturais em tecidos dentários afetados pela hiperbilirrubinemia, normalmente constatada a partir do sinal clínico de icterícia e provoca o desenvolvi-mento de pigmentos intrínsecos esverdeados nas estruturas dentárias. Materiais e Métodos: a amostra foi composta por 31 dentes decíduos dividida em grupo controle (n= 7) e grupo experimental (n= 24). As análises macroscópicas foram efetuadas por meio de fotografias individuais padroniza-das e as radiográficas obtidas com aquisições de imagem a 9 mA, 70 kVp, distância de 8cm, exposição 0,4 segundos e com XDR Sensor®. As imagens foram convertidas pelo software XDR Brasil 3.1.6 e padronizadas pelo programa GIMP 2.10.22. Os dados da média simples do histograma foram analisados pelo teste T-Student e Mann-Whitney (p<0,05). Resultados: demonstraram a maior intensidade de pigmentação em região cervical da raiz, com diferença de densidade radiográfica estaticamente significante na porção radicular entre os grupos experimental e controle (p=0,043). Na análise da densidade radiográfica da estrutura radicular do grupo experimental houve diferença estatica-mente significante (p=0,016) entre os terços cervical e apical. Discussão: Os dados evidenciaram que dentes pigmentados pela hiperbilirrubinemia não possuem alterações na densidade mineral nos terços coronários. Conclusão: Dentes com pigmentação esverdeada bilirrubina possuem diferenças na densidade radiográfica so-mente na região radicular.

Aim: is to identify, through macroscopic and radio-graphic analysis, structural changes in dental tissues affected by hyperbilirubinemia, usually seen from the clinical sign of icterus and causes the development of intrinsic greenish pigments in dental structure. Materials and Methods: The sample consisted of 31 primary teeth divided into a control group (n=7) and an experimental group (n=24). Macroscopic analyzes were performed using standardized individual photographs and radiographic ones obtained by image acquisition at 9 mA, 70 kVp, 8cm distance, 0.4 seconds exposure and with XDR Sensor®. The images were converted by XDR Brasil 3.1.6 software and standardized by GIMP 2.10.22 software. The Histogram's simple mean data were analyzed by T-Student and Mann-Whitney tests (p<0.05). Results: showed intensity of pigmentation in the cervical region of the root, with a statistically significant difference in the root portion between the experimental and control groups (p=0.043. In the analysis of radiographic density of the root structure of the experimental group, there was a statistically significant difference (p= 0.016) between the cervical and apical thirds. Discussion: The data showed that teeth pigmented by hyperbilirubinemia do not have changes in mineral density in the coronary thirds. Conclusion: Greenish pigments teeth have differences in radiographic density only in the root structure.

Manifestações bucais em portadores de epidermólise bolhosa residentes em um município baiano / Oral manifestations of epidermolysis bullosa in a municipality of the state of Bahia

Introdução: a Epidermólise Bolhosa hereditária (EB) é uma doença rara, caracterizada por formações de bolhas na pele e nas mucosas que sofrem mínimos traumas ou aparecem espontaneamente. As principais divisões de EB são Epidermólise Bolhosa Simples, Epidermólise Bolhosa Juncional, Epidermólise Bolhosa Distrófica e a Síndrome de Kindler. As manifestações bucais geralmente encontradas nos pacientes com EB são as bolhas no epitélio oral, microstomia, anquiloglossia, doença periondontal, hipoplasia do esmalte, cárie dentária, atrofia da maxila e prognatismo mandibular, variando para cada tipo da doença. Objetivo: relatar as manifestações bucais dos portadores de Epidermólise Bolhosa residentes no município de Barra da Estiva. Metodologia: trata-se de um estudo transversal, quantitativo e descritivo que foi desenvolvido no município de Barra da Estiva ­ BA com a população de portadores de Epidermólise Bolhosa, através da realização de anamnese e exame clínico. Estatística descritiva foi utilizada para tabular os dados coletados. Resultados: foram analisados 5 portadores de Epidermólise Bolhosa, a maioria do sexo masculino (60%), com média de idade de 5,6 anos. As manifestações bucais encontradas foram bolhas orais (100%), anquiloglossia (100%), língua despapilada (100%), hipoplasia de esmalte (80%), cárie (40%) e abertura de boca limitada em média de 28,6 mm. Conclusão: os portadores de Epidermólise Bolhosa apresentaram manifestações orais características da doença, tendo como consequências maiores dificuldades para realizar higienização bucal e tratamento odontológico, sendo necessário conhecimento prévio dos cirurgiões-dentistas para o atendimento desses pacientes.

Introduction: inherited Epidermolysis Bullosa (EB) is a rare disease, characterized by blistering of the skin and mucous membranes that suffer minimal trauma or appear spontaneously. The main divisions of EB are Simple Epidermolysis Bullosa, Junctional Epidermolysis Bullosa, Dystrophic Epidermolysis Bullosa and Kindler Syndrome. The oral manifestations usually found in patients with EB are blisters in the oral epithelium, microstomy, ankyloglossia, periodontal disease, enamel hypoplasia, dental caries, atrophy of the jaw and mandibular prognathism, varying for each type of disease. Objective: to report the oral manifestations of Epidermolysis Bullosa patients living in the municipality of Barra da Estiva. Methods: cross-sectional study, quantitative and descriptive that was developed in the municipality of Barra da Estiva-BA with the population of people with Epidermolysis Bullosa, through anamnesis and clinical examination. Descriptive statistics was used to tabulate the data collected. Results: 5 children with Epidermolysis Bullosa were analyzed, most male (60%), with an average age of 5,6 years. Oral manifestations found were oral blisters (100%), anquiloglossia (100%), loss of papillae of the tongue (100%), enamel hypoplasia (80%), tooth decay (40%) and mouth opening limited to the average of 28.6 mm. Conclusion: epidermolysis Bullosa children presented oral manifestations common to the disease, leading to difficulties in performing oral hygiene and dental treatment, requiring prior knowledge of dental surgeons for the care of these patients.

Diagnostic methods for stained pits and fissures caries lesions on the occlusal surface / Métodos diagnósticos para lesões de cárie com sulcos pigmentados em superfície oclusal

ABSTRACT Objective: The aim of this study was to compare methods for in vitro diagnosis of pigmented pits and fissures on the occlusal surface. Methods: Forty-one human molars and premolars extracted with pigmentation in pits and fissures were used. The teeth were evaluated with artificial illumination for classification according to ICDAS, followed by fluorescent laser evaluation. For the radiographic evaluation, the teeth were positioned to obtain interproximal images, adopting the criterion of Rodrigues et al. 2008 for diagnosis of lesions. For histological evaluation, the teeth were sectioned in the mesiodistal direction in the occlusal sulcus region and evaluated in a 20-fold stereoscopic magnifying glass, using the criterion of Ekstrand et al. (1997) for evaluation. The methods were compared with the histological evaluation, obtaining values of accuracy, sensitivity and specificity regarding the response variables "presence / absence" of enamel caries. Results: When comparing visual inspection with histological analysis, 65.85% accuracy, 40% sensitivity and 90.48% specificity were observed with false positive and negative probability of 20% and 38.71%. When comparing the fluorescent laser with the histological analysis, the accuracy was 58.54%, sensitivity 70% and specificity 47.62%. Comparing the radiographic analysis with the histological analysis, it was obtained 53.66% accuracy, sensitivity of 42.11% and specificity of 73.68%. Conclusion: The ROC curve and the Yuden index showed that visual inspection presented the best combination of sensitivity and specificity than fluorescent laser and radiographic analysis for diagnosis, which represented the best method for detecting inactive carious lesions in enamel.

RESUMO Objetivo: O objetivo deste estudo foi comparar métodos para diagnóstico in vitro de sulcos pigmentados em superfície oclusal. Métodos: Foram utilizados 41 molares e pré-molares humanos extraídos com pigmentação em sulcos e fissuras. Os dentes foram avaliados com iluminação artificial para classificação quanto ao critério ICDAS, seguida por avaliação com laser fluorescente. Para a avaliação radiográfica, os dentes foram posicionados para obtenção de imagens interproximais, adotando-se o critério de Rodrigues et al. (2008) para diagnóstico. Para avaliação histológica, os dentes foram seccionados no sentido mésio-distal na região de sulco oclusal e avaliados em lupa estereoscópica com aumento de 20 vezes, adotando-se o critério de Ekstrand et al. (1997). Os métodos foram comparados com a avaliação histológica, obtendo-se valores de acurácia, sensibilidade e especificidade quanto às variáveis de resposta "presença/ausência" de lesão de cárie em esmalte. Resultados: Ao comparar a inspeção visual com a análise histológica, observou-se acurácia de 65,85%, sensibilidade de 40% e especificidade de 90,48%. Ao comparar o laser fluorescente com a análise histológica, a acurácia foi de 58,54%, sensibilidade de 70% e especificidade de 47,62%. Na comparação da análise radiográfica com a histológica, obteve-se acurácia de 53,66%, sensibilidade de 42,11% e especificidade de 73,68%. Conclusão: A curva ROC mostrou que a inspeção visual apresentou a melhor combinação de sensibilidade e especificidade que o laser fluorescente e que a análise radiográfica para o diagnóstico, representando o melhor método para detecção de cárie em lesões com sulcos pigmentados em esmalte

The influence of prophylaxis with amino acid glycine powder and sodium bicarbonate jet on the bond strength of dental enamel / A influência da profilaxia com aminoácido glicina em pó e jato de bicarbonato de sódio na resistência de união do esmalte dentário

Aim: To compare the influence of prophylaxis with sodium bicarbonate and amino acid glycine powder on the bond strength of bovine teeth enamel and on the properties of two adhesive systems. Methods:Thirty-six extracted bovine incisors were randomly divided into six groups (n = 6) according to the prophylactic treatment received: no prophylactic treatment (NT), sodium bicarbonate powder (SB), and glycine powder (GL). Each group was subdivided into 2 groups based on what adhesive systems were used: conventional system (A) and universal system (B). Composite resin was applied on the buccal surface of the teeth in a block measurement 8x8x6 mm. The specimens were cut to obtain beams measuring 1.0 x 1.0 mm and were subjected to microtensile bond strength tests. Results were compared using two-way ANOVA (p ≤ 0.05). Results: The GLA group obtained the highest bond strength value for the conventional adhesive (18.97 MPa), but the GLB group obtained a lower strength value than the SBB group (GLB: 21.05 MPa and SBB: 22.29 MPa) (p < 0.05). Conclusions: Cleaning of the enamel surface increases the adhesive properties of restorative materials, and the bond strength was more effective in the group that received glycine prophylaxis and the conventional adhesive system.

Objetivo:Comparar a influência da profilaxia com bicarbonato de sódio e ClinproProphy ™ na resistência de união do esmalte de dentes bovinos e nas propriedades de dois sistemas adesivos.Métodos: Trinta e seis incisivos bovinos extraídos foram divididos aleatoriamente em 6 grupos (n = 6), cada um de acordo com o tratamento profilático recebido: nenhum tratamento profilático (NT), bicarbonato de sódio em pó (SB), glicina em pó (GL). Cada grupo foi subdividido em 2 grupos com base nos sistemas adesivos utilizados: sistema convencional (A) e sistema universal (B). A resina composta foi aplicada na superfície bucal dos dentes em um bloco de 8x8x6 mm. As amostras foram cortadas para obter blocos medindo 1,0 x 1,0 mm e submetidas a testes de resistência de união por microtração. Os resultados foram comparados usando o teste two-way ANOVA (p ≤ 0,05). Resultados: O grupo GLA obteve o maior valor de resistência de união para o adesivo convencional (18,97 MPa), mas o grupo GLB obteve um valor de resistência menor que o grupo SBB (GLB: 21,05 MPa e SBB: 22,29 MPa) (p < 0,05). Conclusão: A limpeza da superfície do esmalte aumenta as propriedades adesivas dos materiais restauradores, e a resistência adesiva foi mais eficaz no grupo que recebeu profilaxia com glicina e sistema adesivo convencional.

Contribution of dentistry in the diagnosis of systemic disorders related to erosive tooth wear / Contribución de la odontología en diagnóstico de trastornos sistémicos relacionados con el desgaste dental erosive / Contribuição da odontologia no diagnóstico de distúrbios sistêmicos relacionados ao desgaste dentário erosivo

Abstract Erosive tooth wear (ETW) is the irreversible loss of dental hard tissue resulting from the chemical-mechanical process. The aim of the present case report was to present two clinical cases of patients affected by ETW arising from different etiological factors. The patients, of the male gender, 9 and 10 years of age presented to the pediatric dental clinic, for routine evaluation. On clinical exam, both patients had no caries lesions, but some lesions suggestive of ETW, which had aspects such as a translucent halo around the occlusal surface of teeth, in addition to "cupping" lesions - mainly in the cusp region, and loss of tooth enamel (by volume). The lesions were restricted to enamel, and the patients showed no dental hypersensitivity. From the dental clinical exam and anamnesis, the two patients were found to have similar tooth structure loss, with diagnosis of ETW. However, in one patient the etiology was extrinsic due to diet, and in the other, it was intrinsic due to gastroesophageal reflux disease (GERD). The latter patient was referred to a specialist for evaluation of the systemic condition, and GERD was diagnosed. It was concluded that dentists play an important role, as coadjuvant in the diagnosis of health problems related to ETW. Therefore, meticulous clinical exams must be performed to establish the correct diagnosis, because swift intervention in the clinical cases presented had a positive impact on halting the erosive process.

Resumen El desgaste dental erosivo corresponde a una pérdida irreversible de tejido duro dental resultante de un proceso químico-mecánico. Este artículo tuvo como objetivo presentar dos casos clínicos de pacientes afectados por desgaste erosivo con diferentes factores etiológicos. Pacientes varones, de 9 y 10 años, acudieron a la clínica dental de odontopediatría para evaluación de rutina. A la exploración clínica, ambos pacientes no presentaban lesiones cariosas y algunas lesiones sugestivas de erosion que presentaban aspectos como un halo translúcido alrededor de la superficie oclusal del diente, además de puntos de punción principalmente en la región cuspídea (lesiones en ventosa) y pérdida del volumen del esmalte dental. Las lesiones se restringieron al esmalte y los pacientes no presentaron hipersensibilidad dentaria. Del examen clínico odontológico y de la anamnesis se aprecia que los dos pacientes presentaban similar pérdida estructural, con diagnóstico de desgaste erosivo, pero un paciente tenía una etiología extrínseca, por alimentación y otro, intrínseco, por trastorno gastroesofágico (TGRE). El paciente fue derivado al especialista para evaluación de la condición sistémica y se diagnosticó la TGRE. Se concluye que el odontólogo tiene un papel importante, como coadyuvante en el diagnóstico de los trastornos de salud relacionados con el desgaste erosivo. Por tanto, se debe realizar un examen clínico minucioso para establecer el diagnóstico correcto, ya que la rápida intervención en los casos clínicos presentados, incidió positivamente en la parálisis del proceso de erosión.

Resumo O desgaste dentário erosivo corresponde a uma perda irreversível do tecido duro dentário resultante de um processo químico-mecânico. O presente artigo teve por objetivo apresentar dois casos clínicos de pacientes afetados pelo desgaste erosivo com fatores etiológicos distintos. Os pacientes do gênero masculino, com 09 e 10 anos, compareceram à clínica odontológica de odontopediatria para avaliação de rotina. Ao exame clínico, ambos os pacientes apresentavam ausência de lesão de cárie e algumas lesões sugestivas de erosão que apresentavam aspectos como halo translúcido ao redor da superfície oclusal do dente, além de pontos socavados principalmente na região de cúspide (lesões de "cupping") e perda do volume do esmalte dentário. As lesões estavam restritas ao esmalte e os pacientes não apresentavam hipersensibilidade dentária. A partir do exame clínico odontológico e anamese pode-se constatar que os dois pacientes apresentavam perdas estruturais semelhantes, com diagnóstico de desgaste erosivo, porém um paciente apresentava etiologia extrínseca, pela alimentação e outro, intrínseca, por distúrbio gastroesofágico (DGRE). O paciente foi encaminhado ao especialista para avaliação do quadro sistêmico, sendo diagnosticado o DGRE. Conclui-se que o cirurgião-dentista tem um papel importante, como coadjuvante no diagnóstico de distúrbios de saúde relacionados ao desgaste erosivo. Portanto, um exame clínico de maneira minuciosa deve ser realizado para estabelecer o diagnóstico correto, visto que, a rápida intervenção nos casos clínicos apresentados, impactaram de forma positiva na paralisação do processo erosivo.

Consideraciones diagnósticas para la exodoncia de primeros molares permanentes severamente afectados por la Hipomineralización de Molares e Incisivos / Considerações diagnósticas para a exodontia de primeiros molares permanentes severamente afetados pela Hipomineralização de Molares e Incisivos / Diagnostic considerations for extraction of first permanent molars severely affected by Molar-Incisor Hypomineralization

Resumen La Hipomineralización de Molares e Incisivos (HMI) es un defecto de desarrollo del esmalte de origen multifactorial que afecta de uno a cuatro primeros molares permanentes y frecuentemente está asociada con incisivos permanentes. Clínicamente se caracteriza por presentar opacidades demarcadas de color blanco-crema y/o amarillo-café. En casos severos puede haber dolor, fracturas posteruptivas, lesiones de caries dental y/o restauraciones atípicas. Entre las opciones de tratamiento se encuentran restauraciones temporales con cemento de ionómero de vidrio, restauraciones en resina compuesta, coronas, restauraciones indirectas y exodoncia. El objetivo de este caso es analizar las consideraciones diagnósticas de la exodoncia de primeros molares permanentes severamente afectados por la HMI. Paciente de sexo femenino, 9 años de edad, patrón esquelético Clase I, maloclusión Clase I bilateral e HMI severa. Para el tratamiento se optó por realizar la exodoncia de los cuatro primeros molares permanentes bajo anestesia general. Luego de 10 meses, se observa que los segundos molares permanentes están clínicamente sanos y presentan inclinaciones y posiciones favorables para el cierre espontáneo del espacio. Se concluye que la exodoncia de primeros molares permanentes severamente afectados por la HMI es una estrategia que mejora el pronóstico del paciente y para realizarla, se requiere trabajar en conjunto con el ortodoncista para diagnosticar y planear individualmente cada caso.

Resumo A Hipomineralização de Molares e Incisivos (HMI) é um defeito de desenvolvimento do esmalte, de origem multifatorial que afecta de um a quatro primeiros molares permanentes e frequentemente está associada aos incisivos permanentes. Clinicamente se caracteriza como opacidades demarcadas de coloração branco-creme e/ou amarelo-café. Em casos severos pode haver dor, fraturas pós-irruptivas, lesões de cárie dentária e restaurações atípicas. Dentre as opções de tratamento estão as restaurações temporárias com cimento de ionômero de vidro, restaurações em resina composta, coroas, restaurações indiretas e a exodontia. Esta última opção permite que o segundo molar permanente se reposicione espontaneamente desde que realizada a tempo, portanto, é considerada uma alternativa viável e custo-efetiva. O objetivo deste caso foi analisar as considerações diagnósticas de exodontia de primeiros molares permanentes severamente afetados pela HMI. Paciente do sexo feminino, 9 anos de idade, padrão esquelético Classe I, maloclusão Classe I bilateral e HMI severa. Para o tratamento, optou-se por realizar a exodontia dos quatro primeiros molares permanentes sob anestesia geral. Após 10 meses, se observa que os segundos molares permanentes estão clinicamente saudáveis e apresentam inclinações e posicionamentos favoráveis para o fechamento espontâneo do espaço. Conclui-se que a exodontia de primeiros molares permanentes melhora o prognóstico do paciente e para realizá-la requer um trabalho em conjunto com o ortodontista para diagnosticas e planejar individualmente cada caso.

Abstract Molar and Incisor Hypomineralization (MIH) is an enamel development defect of multifactorial origin that affects one-to-four permanent first molars and is frequently associated with permanent incisors. Clinically it is characterized by demarcated white-cream and/ or yellow-brown opacities. In severe cases, there may be tooth pain, posteruptive fractures, dental caries lesions, and/ or atypical restorations. Treatment options include temporary restorations with glass ionomer cement, restorations with composite resin, crowns, indirect restorations, and tooth extraction. When extractions are performed at the right time, it allows the spontaneous replacement of the second permanent molar, therefore, it is considered a viable and cost/effective treatment. The objective of this case report is to analyze the diagnostic considerations for the extraction of first permanent molars severely affected by MIH. Female patient, 9 years old, Class I skeletal pattern, Class I malocclusion, and severe MIH. For the treatment, it was decided to perform the extraction of the first four permanent molars under general anesthesia. After 10 months, it is observed that the second permanent molars are clinically healthy and have favorable inclinations and positions for spontaneous closure of the space. It is concluded that the extraction of first permanent molars severely affected by MIH is a strategy that improves the patient's prognosis and to carry out, it is necessary to work together with the orthodontist to diagnose and plan each case individually.

Prevalência e fatores associados a defeitos de desenvolvimento do esmalte em crianças de 5 anos de idade matriculadas em creches na cidade de Teresina, Brasil / Prevalence and factors associated with developmental defects of enamel in five-year-old children enrolled in preschools in the city of Teresina, Brazil

Resumo Introdução Crianças com defeitos de desenvolvimento de esmalte (DDE) são mais suscetíveis à hipersensibilidade dentinária, maloclusões e dificuldades relativas à adesão de materiais restauradores. O conhecimento sobre a prevalência de DDE e seus fatores associados permite aos profissionais obter maior compreensão desse problema de saúde bucal, minimizando, dessa forma, as sequelas e melhorando a saúde bucal e a qualidade de vida dos indivíduos afetados. Objetivo Determinar a prevalência de DDE e seus fatores associados na dentição decídua. Método Trata-se de estudo transversal com amostra probabilística de 566 pré-escolares de 5 anos de idade, matriculados em creches públicas e privadas de Teresina, Piauí, Brasil. Foi aplicado questionário socioeconômico e de história médica da criança aos responsáveis. Os exames clínicos foram conduzidos por um único examinador (kappa = 0,93 para DDE e 0,86 para cárie) que utilizou os índices DDE modificado e ceo-d. Foi realizada a análise descritiva dos dados, além dos testes qui-quadrado e exato de Fisher e a regressão de Poisson, considerando como significativo p ≤ 0,05. Resultados A prevalência de DDE foi de 33,7%. A média de dentes com DDE por criança foi de 3,12 ± 2,23. O tipo mais prevalente de DDE foi opacidade demarcada (9,5%). Os segundos molares superiores foram os dentes mais afetados (11,9%). Houve associação entre DDE e estudar em creche pública (p = 0,026) e cárie (p = 0,012). Crianças com experiência de cárie apresentaram maior prevalência de DDE (RP: 1,29; IC95%: 1,01-1,64). Conclusão A prevalência de DDE na dentição decídua foi de 33,7% e se mostrou associada à experiência de cárie.

Abstract Background Children with Developmental Defects of Enamel (DDE) are more susceptible to dentin hypersensitivity, malocclusions, and difficulties related to the adhesion of restorative materials. Knowledge about the prevalence and factors associated with DDE allows professionals to gain a greater understanding of this oral health problem, minimizing sequelae, improving oral health and quality of life of affected individuals. Objective To determine the prevalence and factors associated with DDE in primary dentition. Method This is a cross-sectional study assessing a random sample of 566 preschool five-year-old children, enrolled in public and private preschools in Teresina, Piauí, Brazil. It was applied the socioeconomic and medical history of the child questionnaire for the parents or guardians. Clinical examinations were conducted by a single examiner (kappa = 0.93 for DDE and 0.86 for caries) that used the modified DDE index and dmft. Descriptive analysis, chi-square and Fisher's exact tests, and Poisson regression were performed, considering significant p ≤ 0.05. Results the prevalence of DDE was 33.7%. The mean DDE teeth per child was 3.12 ± 2.23. The most prevalent type of DDE was demarcated opacity (9.5%). The second molars were the most affected teeth (11.9%). There was an association between DDE and study at public preschool (p = 0.026) and dental caries (p = 0.012). Children with experience of caries were more likely to DDE (PR: 1.29; 95% CI: 1.01 to 1.64). Conclusion prevalence of DDE in the primary dentition was 33.7% and was associated with caries experience.

Crianças e adolescentes quilombolas apresentam alta prevalência de defeitos de desenvolvimento do esmalte / Quilombola children and adolescents show high prevalence of developmental defects of enamel

Resumo Dentes com defeitos de desenvolvimento do esmalte (DDE) apresentam porosidades e/ou irregularidades que os tornam suscetíveis a acúmulo de biofilme e predisposição à cárie e doenças periodontais. O objetivo deste artigo é determinar a prevalência de DDE e fatores associados em crianças e adolescentes residentes em comunidade quilombola. A população foi censitária e composta por indivíduos na faixa etária de 3 a 14 anos. Os responsáveis responderam a questionário contendo dados socioeconômicos demográficos e histórico de agravos durante a gravidez e infância. Foi aplicado o Índice DDE modificado. Foram realizadas análise descritiva e regressão de Poisson com variância robusta (p<0,05). Foram examinados 406 indivíduos. A prevalência de DDE foi de 80,5%, sendo que em dentes decíduos foi de 42,2% e permanentes 61,1%. Houve associação entre DDE e maior idade da criança (RP=1,09; IC95%=1,01-1,17), uso de antibiótico na gravidez (RP=1,14; IC95%=1,07-1,22) e relato de desnutrição durante a primeira infância (RP=1,12; IC95%=1,03-1,22). A prevalência de DDE em crianças e adolecentes da comunidade quilombola foi alta. E os fatores associados foram maior idade da criança, uso de antibióticos na gravidez e desnutrição durante a primeira infância.

Abstract Teeth with developmental defects of enamel (DDE) have porous and/or uneven enamel, making them more susceptible to the build-up of oral biofilm and development of caries and periodontal diseases. The aim of this cross-sectional study was to determine the prevalence of DDE and associated factors among children and adolescents living in a Quilombola community in the Northeast of Brazil. The study population was census-based and comprised individuals aged three to 14 years. The children's parents/guardians answered a questionnaire devised to collect information on socioeconomic and demographic characteristics, health problems during pregnancy and illnesses during early childhood. DDE was diagnosed using the modified DDE index. The data were analyzed using descriptive statistics and Poisson regression with robust standard errors (p<0.05). A total of 406 individuals were examined. DDE prevalence was 80.5%: 42.2% in deciduous teeth and 61.1% in permanent teeth. There was an association between presence of DDE and age (PR=1.09, 95% CI=1.01-1.17), use of antibiotics during pregnancy (PR=1.14, 95% CI=1.07-1.22) and reported malnutrition during early childhood (PR=1.12; 95% CI=1.03-1.22). The findings reveal high prevalence of DDE among children and adolescents living in the Quilombola community. Associated factors were older age, use of antibiotics during pregnancy and malnutrition during early childhood.

Associating the Presence of Structural Defects in Dental Enamel with Children's Health History / Associando a Presença de Alterações de Estrutura no Esmalte Dentário com Histórico de Saúde na Infância

The enamel defects, hypoplasia and hypo mineralization, are classified as dental anomalies of structure, being frequently found in deciduous and permanent dentitions, since the permanent teeth and second deciduous molars finish their total mineralization after the age of three. The aim of the present study was to identify the presence of hypo mineralization and/or enamel hypoplasia and to associate it with respiratory problems in infant patients. Of the 90 patients evaluated, it was found that 23 male children (57.5%) and 22 female children (44%) had defects in the structure of tooth enamel. Most children were born by cesarean operation (64.4%), with no complications during birth (90.0%), 12.2% of children had dental anomalies (agenesis, ectopic canine, ankylosis, fusion, conoid tooth, and macrodontia, only 7 children showed an association between dental anomalies and enamel defects. Regarding respiratory problems that occurred up to 3 years of age, 38.9% had an episode of asthma, bronchitis, sinusitis, rhinitis, or pneumonia, and 55% had similar results at the current age. There was a positive association (Chi-square tests) between the presence of changes in the structure of tooth enamel and the presence of respiratory problems up to 3 years of age (p <0.001). It is concluded, therefore, that the presence of respiratory problems in early childhood, can interfere in amelogenesis, providing disturbances for the formation of normal enamel, causing defects or irregularities in the surface of the dental enamel, such as hypoplasias and hypo mineralization. (AU)

Os defeitos de esmalte, hipoplasia e hipomineralização, são classificados como anomalias dentárias de estrutura, sendo encontrados com frequência nas dentições decídua e permanente, já que os dentes permanentes e segundos molares decíduos finalizam sua total mineralização após os três anos de idade. O objetivo do presente estudo foi identificar a presença de hipomineralização e/ou hipoplasia de esmalte, e associála com problemas respiratórios no paciente infantil. Dos 90 pacientes avaliados, constatou-se que 23 crianças do gênero masculino (57,5%) e 22 do gênero feminino (44%) apresentaram defeitos na estrutura do esmalte dentário. A maioria das crianças nasceu de parto cesária (64,4%), sem complicação no parto (90,0%), 12,2% das crianças apresentaram anomalias dentárias (agenesia, canino ectópico, anquilose, fusão, dente conóide e macrodontia), somente 7 crianças apresentaram associação entre anomalias dentárias e defeitos de esmalte. Em relação à problemas respiratórios ocorrido até aos 3 anos de idade 38,9% apresentaram algum episódio de asma, bronquite, sinusite, rinite ou pneumonia e 55% apresentaram resultados semelhantes na idade atual. Houve associação positiva (Testes Qui Quadrado) entre a presença de alterações na estrutura do esmalte dentário e presença de problemas respiratórios até os 3 anos de idade (p<0,001). Conclui-se, portanto, que a presença de problemas respiratórios na primeira infância, podem interferir na amelogênese, proporcionando distúrbios para formação do esmalte normal, causando defeitos ou irregularidades na superfície do esmalte dentário, como hipoplasias e hipomineralizações. (AU)

Análise da eficácia de dentifrícios clareadores e seus efeitos na superfície dental: um estudo in vitro / Analysis of the effectiveness of whitening dentifrices and their effects on the dental surface: an in vitro study

O clareamento dos dentes pode ser realizado de várias maneiras, em consultório, no âmbito caseiro ou com a utilização de produtos OTC (Over-the-Counter). Dentre esses produtos, existem os dentifrícios clareadores que prometem clarear e prevenir o manchamento dentário. Objetivos: (1) Investigar o potencial clareador e abrasivo de diferentes dentifrícios no esmalte; e (2) avaliar o efeito do dentifrício Oral-B 3D White Perfection® (Oral-B) na prevenção do escurecimento. Materiais e Métodos: Amostras de esmalte bovino foram pigmentadas e escovadas por 14 dias com água (controle negativo) ou com diferentes produtos: Colgate Total 12® (controle), Oral-B, Sensodyne Branqueador Extra Fresh® (Sensodyne) ou Colgate Luminous White Advanced® (Colgate). Oral-B foi testado antes e após pigmentação. As amostras foram avaliadas quanto à cor (espectrofotômetro) e rugosidade superficial (rugosímetro). Para cálculo de alteração de cor (ΔDE00) se utilizou o sistema CIEDE2000. Os dados foram analisados com os testes Kruskal-Wallis, SNK e Mann-Whitney (α=5%). Resultados: O controle negativo apresentou a menor ΔE00 (p<0,05) e o grupo tratado com Sensodyne resultou nos maiores valores (p<0,05). Quanto à rugosidade superficial, não houve diferença significativa entre os grupos avaliados. O dentifrício Oral-B demonstrou efeito protetivo ao manchamento, resultando em menor alteração de cor (p=0,002). Conclusão: Somente o dentifrício Sensodyne apresentou potencial clareador maior que o dentifrício convencional. A escovação prévia com Oral-B reduziu o manchamento dental, embora não tenha prevenido este totalmente de acontecer. Não foram observadas alterações significativas na rugosidade dos dentes após aplicação dos tratamentos, quando comparado ao controle.

Tooth whitening can be performed at the dental office, at-home or upon the use of OTC (Over-the-Counter) pro-ducts. Among the latter, there are whitening toothpastes that promise to bleach and to prevent tooth staining. Objectives: (1) To investigate the bleaching and abrasive potential of different whitening dentifrices to enamel; and (2) to evaluate the effect of Oral-B 3D White Perfection®(Oral-B) toothpaste in preventing staining. Materials and Methods: Bovine enamel samples were stained and brushed for 14 days with water (negative control) or with different products: Colgate Total 12® (control), Oral-B, Sensodyne Branqueador Extra Fresh® (Sensodyne), and Colgate Luminous White Advanced® (Colgate). Oral-B was also tested before and after staining. The samples were tested by their color (spectrophotometer) and surface roughness (profilometer). Color change (ΔDE00) was cal-culated using the CIEDE2000 color system. The data were analyzed using Kruskal-Wallis, SNK, and Mann-Whitney tests (α=5%). Results: The negative control showed the lowest ΔE00 (p<0.05), whereas the group treated with Sensodyne resulted in the greatest color change (p<0.05). For surface roughness, there was not any significant difference among the groups. The Oral-B toothpaste showed a protective effect against staining, resulting in the lowest color change (p=0,002). Conclusion: Only Sensodyne toothpaste showed higher whitening potential than the conventional toothpaste. By using Oral-B prior staining reduced significantly the intensity of staining, although without the complete prevention of this event. Significant differences were not observed after treatment concerning roughness in comparison to the control.

Clinical performance of a micro invasive treatment based on demineralization-remineralization for dental fluorosis: case report

Introduction: Dental fluorosis manifests clinically as white to brown spots on the enamel teeth that were exposed to excessive fluoride during the formation process. Esthetic treatments were described in the literature to reduce or eliminate the fluorotic stains on the enamel surface. Objective: The aim of this study is to present an alternative treatment for fluorosis-stained teeth. Case report: This case report describes the clinical performance of a treatment of a 12-year-old male patient whose teeth presented moderate fluorosis. This treatment is based on tooth demineralization and remineralization. The material has an acid phase made by hydrochloric acid with tricarboxylic acid, and an alkaline phase made by Calcium Hydroxide. Results: This pain less and fast treatment presented good results. The treatment eliminated the spots during the follow-up and preserved most of the dental structure, improving the appearance of the patient's teeth. Conclusion: The appearance of the treated enamel showed a surface almost completely free of fluorotic stains, demonstrating the satisfactory results of this treatment.

Introdução: A fluorose dentária manifesta-se clinicamente como manchas brancas a marrons no esmalte de dentes expostos ao excesso de flúor durante o processo de formação. Tratamentos estéticos foram descritos na literatura para reduzir ou eliminar as manchas fluoróticas na superfície do esmalte. Objetivo: Apresentar uma alternativa de tratamento para dentes manchados por fluorose dentária. Relato do caso: Este relato de caso descreve o desempenho clínico do tratamento para dentes com fluorose moderada em um paciente de 12 anos. Esse tratamento foi baseado numa técnica de desmineralização e remineralização do dente. O material possui uma fase ácida composta por ácido clorídrico com ácido tricarboxílico, e uma fase alcalina composta por Hidróxido de Cálcio. Resultados: Observou-se que esse tratamento, sem dor e rápido, apresentou resultados satisfatórios, pois eliminou as manchas durante o acompanhamento. Além disso, preservou ao máximo a estrutura dentária, beneficiando o paciente com uma melhor aparência dos seus dentes. Conclusão: O aspecto do esmalte tratado mostrou uma superfície quase sem manchas fluoróticas, demonstrando resultados satisfatórios deste tratamento.

Avaliação radiográfica da resposta pulpar e periapical de dentes de cães ao Emdogain® após pulpotomia / Radiographic evaluation of pulpal and periapical response of dogs teeth to Emdogain® used as pulpotomy agent

Introdução: O derivado da matriz do esmalte (Emdogain®) é um extrato de proteína usado para cicatrização periodontal. Objetivo: O objetivo desse estudo foi avaliar radiograficamente a resposta pulpar e periapical de dentes de cães após pulpotomia e uso do gel derivado da matriz do esmalte (Emdogain®). Métodos: A pulpotomia foi realizada em 30 dentes (60 raízes) de 3 cães, e o tecido pulpar remanescente foi recoberto com os seguintes materiais: Grupos 1 e 4: gel derivado da matriz do esmalte (Emdogain®); Grupos 2 e 5: hidróxido de cálcio; Grupos 3 e 6: óxido de zinco e cimento de eugenol. Após 10 dias (Grupos 1-3) e 75 dias (Grupos 4-6) foram obtidas radiografias periapicais e a avaliação radiográfica foi realizada considerando-se: a integridade da lâmina dura, presença de áreas de rarefação óssea periapical, reabsorção radicular (interna e externa) e formação de ponte de dentina. Resultados: No período de 10 dias, todos os espécimes dos Grupos 1-3 apresentaram ausência de rarefação óssea periapical, reabsorção radicular (interna e externa) e formação de ponte dentinária. No período de 75 dias, os Grupos 4-6 não apresentaram formação de ponte dentinária em nenhum espécime. Áreas de rarefação óssea periapical foram observadas em 100% das raízes no Grupo 4, 62,5% das raízes no Grupo 6 e em 25% das raízes nos Grupos 5. Conclusão: O uso do gel derivado da matriz do esmalte (Emdogain®) como material para capeamento após a pulpotomia levou à formação de lesões periapicais e não induziu a deposição de tecido mineralizado (AU).

Introduction: The enamel matrix derivative (Emdogain®) is a protein extract used for periodontal healing. The objective of this study was to evaluate radiographically the pulpal and periapical response of dogs teeth after pulpotomy and use of enamel matrix derivative gel (Emdogain®). Methods: Pulpotomy was performed in 30 teeth (60 roots) from 3 dogs and the remaining pulp tissue was capped with the following materials: Groups 1 and 4: enamel matrix derivative gel (Emdogain®); Groups 2 and 5: calcium hydroxide; Groups 3 and 6: zinc oxide and eugenol cement. After 10 days (Groups 1-3) and 75 days (Groups 4-6) periapical radiographs were obtained and the radiographic evaluation was performed considering the integrity of the lamina dura, presence of areas of periapical bone rarefaction, root resorption (internal and external) and dentin bridge formation. Results: In the 10- day period, all specimens in Groups 1-3 presented absence of periapical bone rarefaction, absence of root resorption (internal and external) and absence of dentin bridge formation. In the 75-day period, Groups 4-6 did not present dentin bridge formation in any specimen. Periapical bone rarefaction areas were observed in 100% of the roots in Group 4, 62,5% of the roots in Group 6 and in 25% of the roots in Groups 5. Conclusion: The use of enamel matrix derivative gel (Emdogain®) as a capping material after pulpotomy lead to formation of periapical lesions and did not induce deposition of mineralized tissue(AU).